Ceramic Ball
Product Number | System of measurement |
Roller Diameter | Material | Hardness | Coefficient Of Thermal Expansion |
Thermal Conductivity | Sphericity | Density | Weight | price | Cart |
---|---|---|---|---|---|---|---|---|---|---|---|
ZrO2-5.0 mm | Metric | 5.0 mm | Zirconia (ZRO2) | 70 HRC | 5.7 x 10–6/°F | 2 W/m-K @ 20° C | 0.25μm | 6.00 g/cm3 | 0.3953g | Inquiry |
|
SiC-20.0 mm | Metric | 20.0 mm | Silicon carbide (SIC) | 85~90 HRC | 2.2 x 10–6/°F | 120 W/m-K @ 20° C | 0.25μm | 3.10 g/cm3 | 13.07g | Inquiry |
|
Al2O3-7.98 mm | Metric | 7.98 mm | Alumina(Al2O3) | 80 HRC | 46 × 10-7/° F | 194.5 Btu/hr. × in./sq. ft./°F @ 212° F | 0.25μm | 3.95 g/cm3 | 1.04g | Inquiry |
|
Si3N4-14.0 mm | Metric | 14.0 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.25μm | 3.20~3.30 g/cm3 | 4.626g | Inquiry |
|
Si3N4-14.0 mm G5 | Metric | 14.0 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.13μm | 3.20~3.30 g/cm3 | 4.626g | Inquiry |
|
SiC-1.0 mm | Metric | 1.0 mm | Silicon carbide (SIC) | 85~90 HRC | 2.2 x 10–6/°F | 120 W/m-K @ 20° C | 0.25μm | 3.10 g/cm3 | 0.00163g | Inquiry |
|
Si3N4-2.0 mm G5 | Metric | 2.0 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.13μm | 3.20~3.30 g/cm3 | 0.01349g | Inquiry |
|
Al2O3-10.0 mm | Metric | 10.0 mm | Alumina(Al2O3) | 80 HRC | 46 × 10-7/° F | 194.5 Btu/hr. × in./sq. ft./°F @ 212° F | 0.25μm | 3.95 g/cm3 | 2.047g | Inquiry |
|
Si3N4-0.8 mm | Metric | 0.8 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.25μm | 3.20~3.30 g/cm3 | 0.00086g | Inquiry |
|
Si3N4-19.0 mm | Metric | 19.0 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.25μm | 3.20~3.30 g/cm3 | 11.56g | Inquiry |
|
Si3N4-19.0 mm G5 | Metric | 19.0 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.13μm | 3.20~3.30 g/cm3 | 11.56g | Inquiry |
|
SiC-2.5 mm | Metric | 2.5 mm | Silicon carbide (SIC) | 85~90 HRC | 2.2 x 10–6/°F | 120 W/m-K @ 20° C | 0.25μm | 3.10 g/cm3 | 0.02553g | Inquiry |
|
ZrO2-7.5 mm | Metric | 7.5 mm | Zirconia (ZRO2) | 70 HRC | 5.7 x 10–6/°F | 2 W/m-K @ 20° C | 0.25μm | 6.00 g/cm3 | 1.3342g | Inquiry |
|
SiC-25.0 mm | Metric | 25.0 mm | Silicon carbide (SIC) | 85~90 HRC | 2.2 x 10–6/°F | 120 W/m-K @ 20° C | 0.25μm | 3.10 g/cm3 | 25.53g | Inquiry |
|
Si3N4-24.0 mm | Metric | 24.0 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.25μm | 3.20~3.30 g/cm3 | 23.31g | Inquiry |
|
Si3N4-24.0 mm G5 | Metric | 24.0 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.13μm | 3.20~3.30 g/cm3 | 23.31g | Inquiry |
|
SiC-5.0 mm | Metric | 5.0 mm | Silicon carbide (SIC) | 85~90 HRC | 2.2 x 10–6/°F | 120 W/m-K @ 20° C | 0.25μm | 3.10 g/cm3 | 0.2042g | Inquiry |
|
ZrO2-9.5 mm | Metric | 9.5 mm | Zirconia (ZRO2) | 70 HRC | 5.7 x 10–6/°F | 2 W/m-K @ 20° C | 0.25μm | 6.00 g/cm3 | 2.69g | Inquiry |
|
Al2O3-14.0 mm | Metric | 14.0 mm | Alumina(Al2O3) | 80 HRC | 46 × 10-7/° F | 194.5 Btu/hr. × in./sq. ft./°F @ 212° F | 0.25μm | 3.95 g/cm3 | 5.618g | Inquiry |
|
Si3N4-2.0 mm | Metric | 2.0 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.25μm | 3.20~3.30 g/cm3 | 0.01349g | Inquiry |
|
SiC-7.5 mm | Metric | 7.5 mm | Silicon carbide (SIC) | 85~90 HRC | 2.2 x 10–6/°F | 120 W/m-K @ 20° C | 0.25μm | 3.10 g/cm3 | 0.6892g | Inquiry |
|
ZrO2-13.0 mm | Metric | 13.0 mm | Zirconia (ZRO2) | 70 HRC | 5.7 x 10–6/°F | 2 W/m-K @ 20° C | 0.25μm | 6.00 g/cm3 | 6.948g | Inquiry |
|
Al2O3-0.8 mm | Metric | 0.8 mm | Alumina(Al2O3) | 80 HRC | 46 × 10-7/° F | 194.5 Btu/hr. × in./sq. ft./°F @ 212° F | 0.25μm | 3.95 g/cm3 | 0.00105g | Inquiry |
|
Al2O3-19.0 mm | Metric | 19.0 mm | Alumina(Al2O3) | 80 HRC | 46 × 10-7/° F | 194.5 Btu/hr. × in./sq. ft./°F @ 212° F | 0.25μm | 3.95 g/cm3 | 14.04g | Inquiry |
|
Si3N4-4.5 mm | Metric | 4.5 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.25μm | 3.20~3.30 g/cm3 | 0.1536g | Inquiry |
|
Si3N4-4.5 mm G5 | Metric | 4.5 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.13μm | 3.20~3.30 g/cm3 | 0.1536g | Inquiry |
|
Si3N4-35.0 mm | Metric | 35.0 mm | Silicon Nitride (Si3N4) | 75~80 HRC | 15 × 10-7/° F | 29 W/m-K @ 20° C | 0.25μm | 3.20~3.30 g/cm3 | 72.29g | Inquiry |
|
ZrO2-18.0 mm | Metric | 18.0 mm | Zirconia (ZRO2) | 70 HRC | 5.7 x 10–6/°F | 2 W/m-K @ 20° C | 0.25μm | 6.00 g/cm3 | 18.44g | Inquiry |
|
Al2O3-2.0 mm | Metric | 2.0 mm | Alumina(Al2O3) | 80 HRC | 46 × 10-7/° F | 194.5 Btu/hr. × in./sq. ft./°F @ 212° F | 0.25μm | 3.95 g/cm3 | 0.01638g | Inquiry |
|
Al2O3-24.0 mm | Metric | 24.0 mm | Alumina(Al2O3) | 80 HRC | 46 × 10-7/° F | 194.5 Btu/hr. × in./sq. ft./°F @ 212° F | 0.25μm | 3.95 g/cm3 | 28.30g | Inquiry |
|
-
show / page